Kf 9795 Adhesion and Sealing of Interior and Exterior Decorative Components of Rail Transit, Subway, and High-Speed Rail Vehicles

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KF 9795
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black, White, and Gray
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KF9795Weathering resistant modified polyurethane sealant is a single component moisture cured modified polyurethane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion to various substrates such as metal and glass

Main purpose
Used for adhesive sealing of interior and exterior decorative parts of vehicle bodies in rail transit, subways, and high-speed railways

Product features

*Environmentally friendly, silicone free, spray painted, and polished

 

*Weathering resistance, good durability, no yellowing

 

*Good extrusion and thixotropy, easy to scratch and modify

 

KF9795
project	Technicalindicators	Typical value
Appear	Black, white, and gray,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.4±0.1	1.48
Extrudabilityg / min GB/T 13477.4	400-800	650
Sagging mm GB/T 13477.6	≤0.5	0
Table drytime2 min GB/T 13477.5	25~50	35
Curing speed mm/d HG/T 4363	≥2.5	2.8
Non-volatile content% GB/T 2793	≥98	99
Hardnes s Shao A GB/ 531.1	40~50	50
Tensile strength MPa GB/T 528	≥2.0	2.5
Fracturelength% GB/T 528	≥350	400
Tear strength N/mm GB/T 529	≥5.0	6.0
Oper ating Temperature /ºC	-40~90