Kt 9331 Adhesion of Reinforcement Ribs for Elevators and Anti-Theft Doors; Adhesive Sealing of Sheet Metal Materials Such as Galvanized Steel and Stainless Stee

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KT 9331
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Aluminum
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black,
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KT 9331High strength modified silane sealant is a single component moisture cured modified silane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion performance to various materials such as metal, galvanized sheet, stainless steel, etc

Main purpose

Used for bonding reinforcement ribs of elevators and anti-theft doors; Adhesive sealing of sheet metal materials such as galvanized steel and stainless steel

Product features

*Environmentally friendly, high modulus, strong initial adhesion

 

*Quick drying of the meter and ability to locate quickly

 

*Good weather resistance, durability, and seismic resistance

KT 9331
project	TECHNICAL INDEX	Typical value
Appear	Black, ,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.45±0.1	1.50
Extrudabilityg / min GB/T 13477.4	400~600	400
droop mm GB/T 13477.6	≤3	0
Table drytime2 min GB/T 13477.5	15~40	20
Curing speed mm/d HG/T 4363	≥3.2	3.5
Non-volatile content% GB/T 2793	≥97	98
Hardnes s Shao A GB/ 531.1	40~55	50
Tensile strength MPa GB/T 528	≥2.5	3.5
Fracturelength% GB/T 528	≥250	300
tensile shear strengthMPa GB/T 7124	≥2.0	2.4
Oper ating Temperature /ºC