Kta 9331 Bonding Reinforcement Ribs of Elevators and Anti-Theft Doors; Adhesive Sealing of Sheet Metal Materials Such as Galvanized Steel and Stainless

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KTA 9331
• Seal Tape Usage: Engineering
• Material: Composite Materials
• Mildew Proof: Not Mildew Proof
• Bonding Material: Aluminum
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black, White, and Gray
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KTA 9331High strength modified silane sealant is a single component moisture cured modified silane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion performance to various materials such as metal, galvanized sheet, stainless steel, etc

Main purpose

bonding reinforcement ribs of elevators and anti-theft doors; Adhesive sealing of sheet metal materials such as galvanized steel and stainless

Product features

*Environmentally friendly, high modulus, strong initial adhesion

 

*Quick drying of the meter and ability to locate quickly

 

*Good weather resistance, durability, and seismic resistance

KTA 9331
project	TECHNICAL INDEX	Typical value
Appear	Black, white, and gray ,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.45±0.1	1.50
Extrudabilityg / min GB/T 13477.4	400~600	500
droop mm GB/T 13477.6	≤3	0
Table drytime2 min GB/T 13477.5	15~40	20
Curing speed mm/d HG/T 4363	≥3.2	3.5
Non-volatile content% GB/T 2793	≥97	98
Hardnes s Shao A GB/ 531.1	40~55	50
Tensile strength MPa GB/T 528	≥2.5	2.9
Fracturelength% GB/T 528	≥250	400
tensile shear strengthMPa GB/T 7124	≥2.0	2.0
Oper ating Temperature /ºC