Kg 9771 Sealing Body Skin and Aluminum Buckle Plate; Adhesion of Interior Decorative Parts of The Vehicle Bodysealing Connection; Sealing of Gaps Passen

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KG 9771
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Aluminum
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black, White, and Gray
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KG 9771 High temperature resistant modified polyurethane sealant is a single component moisture cured modified polyurethane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion with various substrates such as metal and glass.
Main purpose

Sealing of body skin and aluminum buckle plate; Adhesion of interior decorative parts of the vehicle body

Sealing connection; Sealing of gaps in passenger car glass
 

Product features

*Weather resistant, no black water flowing

*Environmentally friendly, solvent-free

*Good extrusion and thixotropy, easy to scratch and modify seams

 

 

KG 9771
project	Technicalindicators	Typical value
Appear	Black, white, and gray,homogeneous paste
Density g/cm3 GB/T 13447.2	1.45±0.1	1.51
Extrudabilityg / min GB/T 13477.4	400-600	550
Sagging mm GB/T 13477.6	≤3	0
Table drytime2 min GB/T 13477.5	40~70	30
Curing speed mm/d HG/T 4363	≥2.5	2.8
Non-volatile content% GB/T 2793	≥95	98
Hardnes s Shao A GB/ 531.1	35~45	40
Tensile strength MPa GB/T 528	≥2.0	2.0
Fracturelength% GB/T 528	≥200	200
Oper ating Temperature /ºC	-40~90