Kga 9791is Aweathering Resistant Modified Silane Sealant a Single Component Moisture Cured Modified Polyurethane Adhesive with Good Sealing Performance and Cohe

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KGA 9791
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black, White, and Gray
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KGA 9791 Weathering resistant modified silane sealant is a single component moisture cured modified polyurethane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion to various substrates such as metal and glass
Main purpose

Weathering resistant modified silane sealant is a single component moisture cured modified polyurethane adhesive with good sealing performance and cohe

Product features

Environmentally friendly, silicone free, spray painted, and polished

 

Good weather resistance, durability, and no yellowing

 

Good extrusion and thixotropy, easy to scratch and modify

KGA 9791
project	Technicalindicators	Typical value
Appear	Black, white, and gray,homogeneous paste
Density g/cm3 GB/T 13447.2	1.45±0.1	1.48
Extrudabilityg / min GB/T 13477.4	400-800	480
Sagging mm GB/T 13477.6	≤0.5	0
Table drytime2 min GB/T 13477.5	15~40	20
Curing speed mm/d HG/T 4363	≥2.5	3.5
Non-volatile content% GB/T 2793	≥98	99
Hardnes s Shao A GB/ 531.1	40~50	50
Tensile strength MPa GB/T 528	≥2.0	3.0
Fracturelength% GB/T 528	≥350	400
tear strengthN/mm GB/T 529	≥5.0	6.0
Oper ating Temperature /ºC	-40~90