Kh 8573 Repair of Bonding and Sealing Between Car Windshields and Side Window Glass, Including Bonding and Sealing at The Integrated Gluing Area of The Glass an

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KH 8573
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black,
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KH 8573 Single component room temperature moisture cured polyurethane adhesive with excellent adhesion and cohesion, non corrosive and non polluting to the adhered substrate, and good adhesion to various substrates such as metal and glass
Main purpose

Repair of bonding and sealing between car windshields and side window glass, including bonding and sealing at the integrated gluing area of the glass and sliding windows

Product features

*High initial strength, fast departure within 2 hours

*Exempt from black primer construction

*Good extrusion and thixotropy, without sagging

KH 8573
project	Typical value
Appear	Black, ,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.36
Extrudabilityg / min GB/T 13477.4	90
Table drytime2 min GB/T 13477.5	20
Curing speed mm/d HG/T 4363	3.4
Non-volatile content% GB/T 2793	98
Hardnes s Shao A GB/ 531.1	60
Tensile strength MPa GB/T 528	6.5
Fracturelength% GB/T 528	450
tensile shear strengthMPa GB/T 7124	3.5
Oper ating Temperature /ºC	-40~90