Kc 8791 Uesd Fling Between The Windshield and Side Window Glass a Passenger Car and The Main Body, as Bonding and Sealing of Interior and Exterior Decorative

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KC 8791
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Aluminum
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black, White, and Gray
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KC 8791 Weathering resistant polyurethane sealant is a single component moisture cured polyurethane adhesive with good sealing performance and cohesion. It has no corrosion or pollution to the substrate, no pollution to the environment, and good adhesion with various substrates such as metal and glass.
Main purpose
ealing between the windshield and side window glass of a passenger car and the main body,  as bonding and sealing of interior and exterior decorative 

Product features

*Weather resistant, no black water flowing

 

*Good extrusion and thixotropy, without sagging

 

*Easy to scratch and modify, without foaming

 

KC 8791
project	Technicalindicators	Typical value
Appear	Black, white, and gray,homogeneous paste
Density g/cm3 GB/T 13447.2	1.3±0.1	1.36
Extrudabilityg / min GB/T 13477.4	80-150	120
Sagging mm GB/T 13477.6	≤0.5	0
Table drytime2 min GB/T 13477.5	≤90	50
Curing speed mm/d HG/T 4363	≥3.0	3.3
Non-volatile content% GB/T 2793	≥97	98
Hardnes s Shao A GB/ 531.1	45~55	50
Tensile strength MPa GB/T 528	≥2.0	4.0
Fracturelength% GB/T 528	≥400	500
Tear strength N/mm GB/T 529	≥10	15
Oper ating Temperature /ºC	-40~90