CG 600 High-End Car, The Adhesion Between The Windshield and The Main Body of The Bus

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: CG 600
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
CG600Quick-drying polyurethane glass adhesive is a one-component moisture curing polyurethane adhesive, which has fast curing speed at low temperature, good cohesion and sealing performance, no corrosion, no pollution to the substrate and no pollution to the environment.

Main purpose
High-grade car, bus windshield structural bonding

Product features
*High initial bond strength, high modulus, 1 h fast positioning
*Low temperature surface drying and fast curing
*Primer Free Construction on Painted Board

 

CG600
project	Technicalindicators	Typical value
Appear	Black,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.2±0.1	1.25
Extrudabilityg / min GB/T 13477.4	40-100	45
Sagging mm GB/T 13477.6	≤0	0
Table drytime2 min GB/T 13477.5	10~30	15
Curing speed mm/d HG/T 4363	≥3.2	4.0
Non-volatile content% GB/T 2793	≥99	99
Hardnes s Shao A GB/ 531.1	50~65	60
Tensile strength MPa GB/T 528	≥7.0	8.0
Fracturelength% GB/T 528	≥10	12.0
Tear strength N/mm GB/T 529	≥200	300
Tensile shear strength MPa GB/T 7124	≥3.5	4.0
Oper ating Temperature /ºC	-40~90