Khc 8882 Adhesion and Sealing of Bus Body Before Electrophoresis of Rice Gold

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KHC 8882
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Aluminum
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KHC 8882 Environmentally friendly polyurethane sealant is a single component moisture cured polyurethane adhesive, environmentally friendly and low VOC, with good sealing performance. It is non corrosive, non polluting to the substrate, non polluting to the environment, and has good adhesion with various substrates such as metal and glass
Main purpose
Adhesion and Sealing of Bus Body Before Electrophoresis of Rice Gold

Product features
*without silicone, and good compatibility with electrophoresis

*High temperature baking and solidification without foaming

*Good adhesion with gold substrate, high strength without silicone, and good compatibility with electrophoresis

 

KHC 8882
project	Technicalindicators	Typical value
Appear	Black, homogeneous paste
Density g/cm3 GB/T 13447.2	1.45±0.1	1.25
Extrudabilityg / min GB/T 13477.4	100-200	100
Sagging mm GB/T 13477.6	≤3	0
Table drytime2 min GB/T 13477.5	60~90	80
Curing speed mm/d HG/T 4363	≥2.5	3.5
Non-volatile content% GB/T 2793	≥99	99
Hardnes s Shao A GB/ 531.1	45~55	50
Tensile strength MPa GB/T 528	≥5.0	7.0
Fracturelength% GB/T 528	≥400	450
Tear strength N/mm GB/T 529	≥6.0	12.0
Oper ating Temperature /ºC	-40~90