CG 100 High-End Cars, Bus Windshield and Side Window Glass Skin Profile Structures and Other High-Strength Structures Are Sticky

• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Seal Tape Usage: Engineering
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: CG 100
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
CG100 Quick-drying polyurethane glass adhesive is a one-component moisture curing polyurethane adhesive, which has fast curing speed at low temperature, good cohesion and sealing performance, no corrosion, no pollution to the substrate and no pollution to the environment.

Main purpose
High-grade car, bus windshield and side window glass, skin, profile structural parts and other high-strength structural bonding.

Product features
*High strength, high elasticity and quick drying
*Environmentally friendly, solvent free
*Good thixotropy, easy construction
 

CG100
project	Technicalindicators	Typical value
Appear	Black,homogeneous paste
Density g/cm3 GB/T 13447.2	1.2±0.1	1.22
Extrudabilityg / min GB/T 13477.4	60-150	60
Sagging mm GB/T 13477.6	≤0	0
Table drytime2 min GB/T 13477.5	15~45	30
Curing speed mm/d HG/T 4363	≥3.0	3.2
Non-volatile content% GB/T 2793	≥99	99
Hardnes s Shao A GB/ 531.1	50~60	55
Tensile strength MPa GB/T 528	≥8.0	9.0
Fracturelength% GB/T 528	≥10	12.0
Tear strength N/mm GB/T 529	≥400	500
Tensile shear strength MPa GB/T 7124	≥4.0	5.0
Oper ating Temperature /ºC	-40~90