Kf 8895 Windshield and Side Window Glass, Skin, Profile Structural Components, and Other High-Strength Structural Adhesives for Rail Transit, Subway, High-Sp

• After-sales Service: Online Technical Support
• Type: Silicone Sealant
• Seal Tape Kind: Liquid Tape
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: KF 8895
• Seal Tape Usage: Engineering
• Material: Composite Materials
• State: Paste
• Mildew Proof: Not Mildew Proof
• Bonding Material: Glass
• Feature2: Strong Durability
• Feature3: Health and Environmental Protection
• Quality Assurance Period: 10 Years
• Specification2: 20piece/Carton
• Capacity of Production: 15000 Carton/Day
• Port1: Qingdao
• Color2: Black
• Color3: One Component
• Transport Package: Carton
• Specification: 300ml/Piece
• Trademark: KAYSDAA
• Origin: China
• HS Code: 3214109000
• Production Capacity: 1000 T
• Package Size: 26.00cm * 20.00cm * 25.00cm
• Package Gross Weight: 10.000kg

Product Description

Product explaination
KF8895High strength polyurethane glass adhesive is a single component moisture cured polyurethane adhesive with good cohesion and sealing performance. It is non corrosive, non polluting to the substrate, and non polluting to the environment
Main purpose
Used for bonding windshield and side window glass, skin, profile structural components, and other high-strength structures in rail transit, subway, and high-speed rail.

Product features

*High strength, high elasticity

 

*Environmentally friendly, solvent-free

 

*Good thixotropy and convenient construction

 

CG600
project	Technicalindicators	Typical value
Appear	Black,Homogeneous paste
Density g/cm3 GB/T 13447.2	1.2±0.1	1.25
Extrudabilityg / min GB/T 13477.4	40-100	50
Sagging mm GB/T 13477.6	≤0	0
Table drytime2 min GB/T 13477.5	25~45	30
Curing speed mm/d HG/T 4363	≥3.0	3.2
Non-volatile content% GB/T 2793	≥99	99
Hardnes s Shao A GB/ 531.1	50~60	55
Tensile strength MPa GB/T 528	≥8.0	9.0
Fracturelength% GB/T 528	≥400	500
Tear strength N/mm GB/T 529	≥10.0	12.0
Tensile shear strength MPa GB/T 7124	≥4.5	5.0
Oper ating Temperature /ºC	-40~90